PEKA Build Materials
1 / 5
| Model NO. | AE1 |
| Thermal Conductivity | ≤0.021W/M. K (at 25ºC) |
| Maximum Operating Temperature | 1200 ºC |
| Combustibility | Grade A (Completely Non-Combustible) |
| Hydrophobic | >99% |
| Vibration Mass Loss Rate | ≤1.0 |
| Compression Rebound Rate | >90 |
| Material | Glass Fiber, Silica |
| Density | 200 ± 30 Kg/M3 |
| Usage | Oil Pipeline, Wall Insulation |
| Transport Package | Rolls |
Utilizing nano-aerogel and glass fiber composite technology combined with chemical film-forming processes, this product is an innovative material offering superior fireproofing and thermal insulation. The aerogel composite material is composed of nano aerogel, glass fiber, pre-oxidized fiber, and other base materials, perfectly combining excellent performance with flexible bases.
Replaces traditional supercritical extraction, enhancing aerogel penetration and adhesion.
Reduces production costs while improving product stability.
| Item Parameter | Value |
|---|---|
| Thermal Conductivity | 0.018-0.023 W/(m·K) |
| Fireproof Rating | A1 (GB/T 25352-2010) |
| Operating Temperature | -200°C to 650°C |
| Long-Term Shrinkage | ≤1% (650°C) |
| Density | 160-240 kg/m³ |
| Water Absorption | ≤0.02% |
Ultra-low thermal conductivity (1/5 of traditional materials), effectively blocking heat transfer.
A1 fireproof certification, withstands direct flame at 1200°C-1600°C without deformation.
Weather resistance with a lifespan exceeding 20 years; no melting or powdering.
Ultra-light density (160-240 kg/m³), 100% recyclable, and zero toxic emissions.
The thermal insulation performance of air gel felt is far superior to that of conventional materials. Its interior is a nano-porous structure with high porosity and small pore diameter, which can effectively block the flow of air. The thermal conductivity is extremely low, greatly improving the thermal efficiency of equipment.
📦 Fast Delivery: Samples shipped within 3 days; bulk orders delivered in 15-20 days.
🛠️ Support: Installation guidance and lifetime technical consultation.